Även om titanmetallmaterial har visat breda tillämpningsutsikter inom många områden, finns det fortfarande brister i den aktuella forskningen om den heta kontinuerliga rullningsprocessen för titanrör med små diameter, såväl som värmebehandling och mikrostrukturanalys av rullade staplar . Följande kommer att genomföra en detaljerad analys av rullningsprocessen och egenskaper av titan från Titan Material från ASPELTER och MICOSTURE AV ROLLING AV ROLLING AV ROLLING AV RULLING AV ROLLING AV RULLING OCH MICROSTURES OF ASPELING OF ASPELLERINGS OCH Förhållandet mellan rullningsprocess och prestanda .
- Optimalt urval av rullningstemperatur och töjningshastighet
Considering the reduction of deformation resistance, improvement of formability, and guarantee of final rolling structure performance, 950℃was determined as the suitable rolling temperature for titanium tubes. Rolling at this temperature can effectively balance the deformation resistance and plastic deformation capacity of the material. It can make the rolling process smoother, reduce equipment energy consumption and roller wear, and facilitate the attainment av idealisk mikrostruktur och egenskaper .
Samtidigt kan en rimlig belastningshastighet hjälpa till att kontrollera den dynamiska omkristallisationsprocessen för materialet, göra kornen finare och förbättra styrkan och segheten hos materialet . så att materialet helt kan utöva sin plasticitet för att erhålla enhetlig mikrostruktur och utmärkta mekaniska egenskaper .}
- Mikrostrukturegenskaper för heta kontinuerliga rullade produkter med en trepår Y-typ rullande kvarn
Med användning av en trepår Y-typ rullande kvarn för varm kontinuerlig rullning, medelstora staplar med diametrar på 12 mm och 6mm erhölls framgångsrikt .
For the 12mm medium-sized tube, its microstructure presents an equiaxed primary phase transformation microstructure, with grain diameters of approximately 3 - 10μm. This equiaxed structure has good isotropy and can provide relatively uniform mechanical properties in different directions. While for the 6mm medium-sized tube, the microstructure consists of a small amount of equiaxed primary phase, fine strip-like phase, and transformation microstructure, with grain sizes less than 1μm. This is because in the rolling process, the large deformation amount promotes the dynamic recrystallization of the material, and leads to grain refinement. This change not only enhances the strength of the material and improves its plasticity and toughness, but also improves the comprehensive performance of Materialet .
- Verifiering av överensstämmelsen mellan rullningsprocess och produktprestanda
After comprehensive testing and analysis of the microstructure and mechanical properties of titanium tubes rolled by the three-roll Y-type rolling mill, the results show that both the microstructure and mechanical properties meet the technical requirements. This fully proves that the rolling equipment, rolling process parameters, and heat treatment system adopted in the experiment are scientifically reasonable, capable of producing stable and high-quality Titan Tube -produkter . Detta forskningsresultat ger en solid teknisk grund för att ytterligare främja industriproduktionen av titanmetallmaterial, hjälpa till att öka produktionseffektiviteten, minska produktionskostnaderna och främja den bredare tillämpningen av titanmetallmaterial i fler fält .}
Through in-depth research on the rolling process and properties of titanium metal materials, we have clarified the appropriate rolling temperature and strain rate, mastered the microstructure characteristics of different-sized tube materials, and verified the conformity between the rolling process and product performance. These research results are of great significance for optimizing the rolling process of titanium metal materials, improving product quality and performance, and will inject new impetus into the development of the Titanium Metal Materials Industry .